-    MERWINITE     -    Ca3Mg(SiO4)2

 

Crystal Structure 


Because of the translational symmetry all the calculations are performed in the primitive unit cell and not in the conventional unit cell. The following information regarding the structure is given with respect to this primitive unit cell, which sometimes can take an unintuitive shape.

Symmetry (experimental): 

Space group:  14  P2_1/a 
Lattice parameters (Å):  13.2540  5.2930  9.3280 
Angles (°):  90.0  91.9  90.0 

Symmetry (theoretical): 

Space group:  14  P2_1/a 
Lattice parameters (Å):  13.3168  5.2829  9.3039 
Angles (°):  90.0  92.3  90.0 

Cell contents: 

Number of atoms:  56 
Number of atom types: 
Chemical composition: 

Atomic positions (theoretical):

Ca:  0.2590  0.1779  0.2163 
Ca:  0.0795  0.2243  0.9266 
Ca:  0.0965  0.7368  0.4253 
Mg:  0.0054  0.2577  0.2537 
Si:  0.1312  0.2311  0.6027 
Si:  0.1404  0.7270  0.0928 
O:  0.0722  0.2156  0.4471 
O:  0.0623  0.4210  0.6957 
O:  0.1220  0.9540  0.6784 
O:  0.2394  0.3611  0.5987 
O:  0.0757  0.7064  0.9403 
O:  0.2530  0.8090  0.0635 
O:  0.1254  0.4724  0.1844 
O:  0.0839  0.9597  0.1734 
Ca:  0.2410  0.6779  0.7837 
Ca:  0.4205  0.7243  0.0734 
Ca:  0.4035  0.2368  0.5747 
Mg:  0.4946  0.7577  0.7463 
Si:  0.3688  0.7311  0.3973 
Si:  0.3596  0.2270  0.9072 
O:  0.4278  0.7156  0.5529 
O:  0.4377  0.9210  0.3043 
O:  0.3780  0.4540  0.3216 
O:  0.2606  0.8611  0.4013 
O:  0.4243  0.2064  0.0597 
O:  0.2470  0.3090  0.9365 
O:  0.3746  0.9724  0.8156 
O:  0.4161  0.4597  0.8266 
Ca:  0.7410  0.8221  0.7837 
Ca:  0.9205  0.7757  0.0734 
Ca:  0.9035  0.2632  0.5747 
Mg:  0.9946  0.7423  0.7463 
Si:  0.8688  0.7689  0.3973 
Si:  0.8596  0.2730  0.9072 
O:  0.9278  0.7844  0.5529 
O:  0.9377  0.5790  0.3043 
O:  0.8780  0.0460  0.3216 
O:  0.7606  0.6389  0.4013 
O:  0.9243  0.2936  0.0597 
O:  0.7470  0.1910  0.9365 
O:  0.8746  0.5276  0.8156 
O:  0.9161  0.0403  0.8266 
Ca:  0.7590  0.3221  0.2163 
Ca:  0.5795  0.2757  0.9266 
Ca:  0.5965  0.7632  0.4253 
Mg:  0.5054  0.2423  0.2537 
Si:  0.6312  0.2689  0.6027 
Si:  0.6404  0.7730  0.0928 
O:  0.5722  0.2844  0.4471 
O:  0.5623  0.0790  0.6957 
O:  0.6220  0.5460  0.6784 
O:  0.7394  0.1389  0.5987 
O:  0.5757  0.7936  0.9403 
O:  0.7530  0.6910  0.0635 
O:  0.6254  0.0276  0.1844 
O:  0.5839  0.5403  0.1734 
Atom type 

We have listed here the reduced coordinates of all the atoms in the primitive unit cell.
It is enough to know only the position of the atoms from the assymetrical unit cell and then use the symmetry to build the whole crystal structure.

Visualization of the crystal structure: 

Size:

  
Nx:  Ny:  Nz:    
You can define the size of the supercell to be displayed in the jmol panel as integer translations along the three crys­tallo­gra­phic axis.
Please note that the structure is represented using the pri­mi­tive cell, and not the conventional one.