-    BERYLLONITE     -    NaBePO4

 

Crystal Structure 


Because of the translational symmetry all the calculations are performed in the primitive unit cell and not in the conventional unit cell. The following information regarding the structure is given with respect to this primitive unit cell, which sometimes can take an unintuitive shape.

Symmetry (experimental): 

Space group:  14  P2_1/n 
Lattice parameters (Å):  8.1599  7.7948  14.0867 
Angles (°):  90  90  90 

Symmetry (theoretical): 

Space group:  14  P2_1/n 
Lattice parameters (Å):  7.9611  7.6311  13.8841 
Angles (°):  90  90  90 

Cell contents: 

Number of atoms:  84 
Number of atom types: 
Chemical composition: 

Atomic positions (theoretical):

Na:  0.2470  0.0028  0.2491 
Na:  0.7343  0.4667  0.0889 
Na:  0.7686  0.0377  0.0692 
Be:  0.9205  0.1662  0.2398 
Be:  0.1001  0.6667  0.0803 
Be:  0.4327  0.1668  0.0911 
P:  0.9212  0.7838  0.2366 
P:  0.1074  0.2883  0.0810 
P:  0.4333  0.7863  0.0920 
O:  0.4349  0.2658  0.1909 
O:  0.0684  0.2687  0.1881 
O:  0.2510  0.7740  0.1261 
O:  0.7439  0.2480  0.2111 
O:  0.9482  0.2514  0.0223 
O:  0.5604  0.2551  0.0160 
O:  0.9443  0.6583  0.1519 
O:  0.2455  0.1605  0.0512 
O:  0.5446  0.6588  0.1478 
O:  0.9253  0.9708  0.1977 
O:  0.1699  0.4740  0.0623 
O:  0.4969  0.9718  0.1106 
Na:  0.2530  0.5028  0.2509 
Na:  0.7657  0.9667  0.4111 
Na:  0.7314  0.5377  0.4308 
Be:  0.5795  0.6662  0.2602 
Be:  0.3999  0.1667  0.4197 
Be:  0.0673  0.6668  0.4089 
P:  0.5788  0.2838  0.2634 
P:  0.3926  0.7883  0.4190 
P:  0.0667  0.2863  0.4080 
O:  0.0651  0.7658  0.3091 
O:  0.4316  0.7687  0.3119 
O:  0.2490  0.2740  0.3739 
O:  0.7561  0.7480  0.2889 
O:  0.5518  0.7514  0.4777 
O:  0.9396  0.7551  0.4840 
O:  0.5557  0.1583  0.3481 
O:  0.2545  0.6605  0.4488 
O:  0.9554  0.1588  0.3522 
O:  0.5747  0.4708  0.3023 
O:  0.3301  0.9740  0.4377 
O:  0.0031  0.4718  0.3894 
Na:  0.7530  0.9972  0.7509 
Na:  0.2657  0.5333  0.9111 
Na:  0.2314  0.9623  0.9308 
Be:  0.0795  0.8338  0.7602 
Be:  0.8999  0.3333  0.9197 
Be:  0.5673  0.8332  0.9089 
P:  0.0788  0.2162  0.7634 
P:  0.8926  0.7117  0.9190 
P:  0.5667  0.2137  0.9080 
O:  0.5651  0.7342  0.8091 
O:  0.9316  0.7313  0.8119 
O:  0.7490  0.2260  0.8739 
O:  0.2561  0.7520  0.7889 
O:  0.0518  0.7486  0.9777 
O:  0.4396  0.7449  0.9840 
O:  0.0557  0.3417  0.8481 
O:  0.7545  0.8395  0.9488 
O:  0.4554  0.3412  0.8522 
O:  0.0747  0.0292  0.8023 
O:  0.8301  0.5260  0.9377 
O:  0.5031  0.0282  0.8894 
Na:  0.7470  0.4972  0.7491 
Na:  0.2343  0.0333  0.5889 
Na:  0.2686  0.4623  0.5692 
Be:  0.4205  0.3338  0.7398 
Be:  0.6001  0.8333  0.5803 
Be:  0.9327  0.3332  0.5911 
P:  0.4212  0.7162  0.7366 
P:  0.6074  0.2117  0.5810 
P:  0.9333  0.7137  0.5920 
O:  0.9349  0.2342  0.6909 
O:  0.5684  0.2313  0.6881 
O:  0.7510  0.7260  0.6261 
O:  0.2439  0.2520  0.7111 
O:  0.4482  0.2486  0.5223 
O:  0.0604  0.2449  0.5160 
O:  0.4443  0.8417  0.6519 
O:  0.7455  0.3395  0.5512 
O:  0.0446  0.8412  0.6478 
O:  0.4253  0.5292  0.6977 
O:  0.6699  0.0260  0.5623 
O:  0.9969  0.5282  0.6106 
Atom type 

We have listed here the reduced coordinates of all the atoms in the primitive unit cell.
It is enough to know only the position of the atoms from the assymetrical unit cell and then use the symmetry to build the whole crystal structure.

Visualization of the crystal structure: 

Size:

  
Nx:  Ny:  Nz:    
You can define the size of the supercell to be displayed in the jmol panel as integer translations along the three crys­tallo­gra­phic axis.
Please note that the structure is represented using the pri­mi­tive cell, and not the conventional one.