-    TERNESITE     -    Ca5(SiO4)2SO4

 

Crystal Structure 


Because of the translational symmetry all the calculations are performed in the primitive unit cell and not in the conventional unit cell. The following information regarding the structure is given with respect to this primitive unit cell, which sometimes can take an unintuitive shape.

Symmetry (experimental): 

Space group:  62  Pnma 
Lattice parameters (Å):  6.8630  15.3870  10.1810 
Angles (°):  90  90  90 

Symmetry (theoretical): 

Space group:  62  Pnma 
Lattice parameters (Å):  6.9225  15.2669  10.1730 
Angles (°):  90  90  90 

Cell contents: 

Number of atoms:  80 
Number of atom types: 
Chemical composition: 

Atomic positions (theoretical):

Ca:  0.0480  0.2500  0.1934 
Ca:  0.1421  0.9041  0.1582 
Ca:  0.3621  0.0867  0.0658 
Si:  0.3451  0.0748  0.3650 
S:  0.0184  0.2500  0.5877 
O:  0.2289  0.2500  0.6089 
O:  0.9645  0.2500  0.4470 
O:  0.9349  0.1701  0.6462 
O:  0.3836  0.9908  0.2692 
O:  0.1818  0.0520  0.4737 
O:  0.2880  0.1541  0.2671 
O:  0.5290  0.1096  0.4515 
Ca:  0.4520  0.7500  0.6934 
Ca:  0.3579  0.0959  0.6582 
Ca:  0.1379  0.9133  0.5658 
Si:  0.1549  0.9252  0.8650 
S:  0.4816  0.7500  0.0877 
O:  0.2711  0.7500  0.1089 
O:  0.5355  0.7500  0.9470 
O:  0.5651  0.8299  0.1462 
O:  0.1164  0.0092  0.7692 
O:  0.3182  0.9480  0.9737 
O:  0.2120  0.8459  0.7671 
O:  0.9710  0.8904  0.9515 
Ca:  0.9520  0.7500  0.8066 
Ca:  0.8579  0.4041  0.8418 
Ca:  0.6379  0.5867  0.9342 
Si:  0.6549  0.5748  0.6350 
S:  0.9816  0.7500  0.4123 
O:  0.7711  0.7500  0.3911 
O:  0.0355  0.7500  0.5530 
O:  0.0651  0.6701  0.3538 
O:  0.6164  0.4908  0.7308 
O:  0.8182  0.5520  0.5263 
O:  0.7120  0.6541  0.7329 
O:  0.4710  0.6096  0.5485 
Ca:  0.5480  0.2500  0.3066 
Ca:  0.6421  0.5959  0.3418 
Ca:  0.8621  0.4133  0.4342 
Si:  0.8451  0.4252  0.1350 
S:  0.5184  0.2500  0.9123 
O:  0.7289  0.2500  0.8911 
O:  0.4645  0.2500  0.0530 
O:  0.4349  0.3299  0.8538 
O:  0.8836  0.5092  0.2308 
O:  0.6818  0.4480  0.0263 
O:  0.7880  0.3459  0.2329 
O:  0.0290  0.3904  0.0485 
Ca:  0.8579  0.0959  0.8418 
Ca:  0.6379  0.9133  0.9342 
Si:  0.6549  0.9252  0.6350 
O:  0.0651  0.8299  0.3538 
O:  0.6164  0.0092  0.7308 
O:  0.8182  0.9480  0.5263 
O:  0.7120  0.8459  0.7329 
O:  0.4710  0.8904  0.5485 
Ca:  0.6421  0.9041  0.3418 
Ca:  0.8621  0.0867  0.4342 
Si:  0.8451  0.0748  0.1350 
O:  0.4349  0.1701  0.8538 
O:  0.8836  0.9908  0.2308 
O:  0.6818  0.0520  0.0263 
O:  0.7880  0.1541  0.2329 
O:  0.0290  0.1096  0.0485 
Ca:  0.1421  0.5959  0.1582 
Ca:  0.3621  0.4133  0.0658 
Si:  0.3451  0.4252  0.3650 
O:  0.9349  0.3299  0.6462 
O:  0.3836  0.5092  0.2692 
O:  0.1818  0.4480  0.4737 
O:  0.2880  0.3459  0.2671 
O:  0.5290  0.3904  0.4515 
Ca:  0.3579  0.4041  0.6582 
Ca:  0.1379  0.5867  0.5658 
Si:  0.1549  0.5748  0.8650 
O:  0.5651  0.6701  0.1462 
O:  0.1164  0.4908  0.7692 
O:  0.3182  0.5520  0.9737 
O:  0.2120  0.6541  0.7671 
O:  0.9710  0.6096  0.9515 
Atom type 

We have listed here the reduced coordinates of all the atoms in the primitive unit cell.
It is enough to know only the position of the atoms from the assymetrical unit cell and then use the symmetry to build the whole crystal structure.

Visualization of the crystal structure: 

Size:

  
Nx:  Ny:  Nz:    
You can define the size of the supercell to be displayed in the jmol panel as integer translations along the three crys­tallo­gra­phic axis.
Please note that the structure is represented using the pri­mi­tive cell, and not the conventional one.