-    ENSTATITE     -    MgSiO3

 

Crystal Structure 


Because of the translational symmetry all the calculations are performed in the primitive unit cell and not in the conventional unit cell. The following information regarding the structure is given with respect to this primitive unit cell, which sometimes can take an unintuitive shape.

Symmetry (experimental): 

Space group:  61  Pbca 
Lattice parameters (Å):  18.2330  8.8191  5.1802 
Angles (°):  90  90  90 

Symmetry (theoretical): 

Space group:  61  Pbca 
Lattice parameters (Å):  17.9591  8.6470  5.0949 
Angles (°):  90  90  90 

Cell contents: 

Number of atoms:  80 
Number of atom types: 
Chemical composition: 

Atomic positions (theoretical):

Mg:  0.3761  0.6560  0.8590 
Mg:  0.3772  0.4859  0.3514 
Si:  0.2714  0.3429  0.0451 
Si:  0.4729  0.3378  0.8030 
O:  0.1827  0.3405  0.0266 
O:  0.3111  0.5050  0.0355 
O:  0.3036  0.2195  0.8302 
O:  0.5622  0.3393  0.8059 
O:  0.4324  0.4833  0.6849 
O:  0.4464  0.1907  0.6125 
Mg:  0.1239  0.3440  0.3590 
Mg:  0.1228  0.5141  0.8514 
Si:  0.2286  0.6571  0.5451 
Si:  0.0271  0.6622  0.3030 
O:  0.3173  0.6595  0.5266 
O:  0.1889  0.4950  0.5355 
O:  0.1964  0.7805  0.3302 
O:  0.9378  0.6607  0.3059 
O:  0.0676  0.5167  0.1849 
O:  0.0536  0.8093  0.1125 
Mg:  0.6239  0.1560  0.6410 
Mg:  0.6228  0.9859  0.1486 
Si:  0.7286  0.8429  0.4549 
Si:  0.5271  0.8378  0.6970 
O:  0.8173  0.8405  0.4734 
O:  0.6889  0.0050  0.4645 
O:  0.6964  0.7195  0.6698 
O:  0.4378  0.8393  0.6941 
O:  0.5676  0.9833  0.8151 
O:  0.5536  0.6907  0.8875 
Mg:  0.8761  0.8440  0.1410 
Mg:  0.8772  0.0141  0.6486 
Si:  0.7714  0.1571  0.9549 
Si:  0.9729  0.1622  0.1970 
O:  0.6827  0.1595  0.9734 
O:  0.8111  0.9950  0.9645 
O:  0.8036  0.2805  0.1698 
O:  0.0622  0.1607  0.1941 
O:  0.9324  0.0167  0.3151 
O:  0.9464  0.3093  0.3875 
Mg:  0.6239  0.3440  0.1410 
Mg:  0.6228  0.5141  0.6486 
Si:  0.7286  0.6571  0.9549 
Si:  0.5271  0.6622  0.1970 
O:  0.8173  0.6595  0.9734 
O:  0.6889  0.4950  0.9645 
O:  0.6964  0.7805  0.1698 
O:  0.4378  0.6607  0.1941 
O:  0.5676  0.5167  0.3151 
O:  0.5536  0.8093  0.3875 
Mg:  0.8761  0.6560  0.6410 
Mg:  0.8772  0.4859  0.1486 
Si:  0.7714  0.3429  0.4549 
Si:  0.9729  0.3378  0.6970 
O:  0.6827  0.3405  0.4734 
O:  0.8111  0.5050  0.4645 
O:  0.8036  0.2195  0.6698 
O:  0.0622  0.3393  0.6941 
O:  0.9324  0.4833  0.8151 
O:  0.9464  0.1907  0.8875 
Mg:  0.3761  0.8440  0.3590 
Mg:  0.3772  0.0141  0.8514 
Si:  0.2714  0.1571  0.5451 
Si:  0.4729  0.1622  0.3030 
O:  0.1827  0.1595  0.5266 
O:  0.3111  0.9950  0.5355 
O:  0.3036  0.2805  0.3302 
O:  0.5622  0.1607  0.3059 
O:  0.4324  0.0167  0.1849 
O:  0.4464  0.3093  0.1125 
Mg:  0.1239  0.1560  0.8590 
Mg:  0.1228  0.9859  0.3514 
Si:  0.2286  0.8429  0.0451 
Si:  0.0271  0.8378  0.8030 
O:  0.3173  0.8405  0.0266 
O:  0.1889  0.0050  0.0355 
O:  0.1964  0.7195  0.8302 
O:  0.9378  0.8393  0.8059 
O:  0.0676  0.9833  0.6849 
O:  0.0536  0.6907  0.6125 
Atom type 

We have listed here the reduced coordinates of all the atoms in the primitive unit cell.
It is enough to know only the position of the atoms from the assymetrical unit cell and then use the symmetry to build the whole crystal structure.

Visualization of the crystal structure: 

Size:

  
Nx:  Ny:  Nz:    
You can define the size of the supercell to be displayed in the jmol panel as integer translations along the three crys­tallo­gra­phic axis.
Please note that the structure is represented using the pri­mi­tive cell, and not the conventional one.