-    CLINOBEHOITE     -    BeOH2

 

Crystal Structure 


Because of the translational symmetry all the calculations are performed in the primitive unit cell and not in the conventional unit cell. The following information regarding the structure is given with respect to this primitive unit cell, which sometimes can take an unintuitive shape.

Symmetry (experimental): 

Space group:  P2_1 
Lattice parameters (Å):  11.0200  4.7460  8.6460 
Angles (°):  90  98.94  90 

Symmetry (theoretical): 

Space group:  P2_1 
Lattice parameters (Å):  10.8424  4.4972  8.2937 
Angles (°):  90  100.32  90 

Cell contents: 

Number of atoms:  60 
Number of atom types: 
Chemical composition: 

Atomic positions (theoretical):

Be:  0.3221  0.5705  0.4174 
Be:  0.3246  0.0696  0.2282 
Be:  0.3237  0.3662  0.9171 
Be:  0.6776  0.3685  0.2731 
Be:  0.9133  0.2005  0.4787 
Be:  0.0868  0.2149  0.0215 
O:  0.3764  0.2424  0.4005 
O:  0.3685  0.7416  0.2711 
O:  0.3823  0.7325  0.5847 
O:  0.1760  0.5687  0.4052 
O:  0.3842  0.2113  0.0847 
O:  0.1762  0.0872  0.1818 
O:  0.3709  0.6980  0.9011 
O:  0.1714  0.3298  0.8878 
O:  0.3629  0.1981  0.7669 
O:  0.0034  0.9545  0.4231 
O:  0.0023  0.4697  0.0778 
O:  0.8294  0.3220  0.3057 
H:  0.3719  0.0884  0.4843 
H:  0.6317  0.3498  0.0133 
H:  0.6117  0.8363  0.3117 
H:  0.3909  0.6020  0.1914 
H:  0.1470  0.3927  0.3387 
H:  0.5230  0.2467  0.4057 
H:  0.9675  0.8776  0.3154 
H:  0.1466  0.9066  0.2295 
H:  0.8356  0.1552  0.2282 
H:  0.8342  0.6637  0.1929 
H:  0.9666  0.3977  0.1700 
H:  0.4783  0.1997  0.0963 
Be:  0.6779  0.0705  0.5826 
Be:  0.6754  0.5696  0.7718 
Be:  0.6763  0.8662  0.0829 
Be:  0.3224  0.8685  0.7269 
Be:  0.0867  0.7005  0.5213 
Be:  0.9132  0.7149  0.9785 
O:  0.6236  0.7424  0.5995 
O:  0.6315  0.2416  0.7289 
O:  0.6177  0.2325  0.4153 
O:  0.8240  0.0687  0.5948 
O:  0.6158  0.7113  0.9153 
O:  0.8238  0.5872  0.8182 
O:  0.6291  0.1980  0.0989 
O:  0.8286  0.8298  0.1122 
O:  0.6371  0.6981  0.2331 
O:  0.9966  0.4545  0.5769 
O:  0.9977  0.9697  0.9222 
O:  0.1706  0.8220  0.6943 
H:  0.6281  0.5884  0.5157 
H:  0.3683  0.8498  0.9867 
H:  0.3883  0.3363  0.6883 
H:  0.6091  0.1020  0.8086 
H:  0.8530  0.8927  0.6613 
H:  0.4770  0.7467  0.5943 
H:  0.0325  0.3776  0.6846 
H:  0.8534  0.4066  0.7705 
H:  0.1644  0.6552  0.7718 
H:  0.1658  0.1637  0.8071 
H:  0.0334  0.8977  0.8300 
H:  0.5217  0.6997  0.9037 
Atom type 

We have listed here the reduced coordinates of all the atoms in the primitive unit cell.
It is enough to know only the position of the atoms from the assymetrical unit cell and then use the symmetry to build the whole crystal structure.

Visualization of the crystal structure: 

Size:

  
Nx:  Ny:  Nz:    
You can define the size of the supercell to be displayed in the jmol panel as integer translations along the three crys­tallo­gra­phic axis.
Please note that the structure is represented using the pri­mi­tive cell, and not the conventional one.