-    LINTISITE     -    Na3LiTi2(Si2O6)22H2O

 

Crystal Structure 


Because of the translational symmetry all the calculations are performed in the primitive unit cell and not in the conventional unit cell. The following information regarding the structure is given with respect to this primitive unit cell, which sometimes can take an unintuitive shape.

Symmetry (experimental): 

Space group:  15  C2/c 
Lattice parameters (Å):  28.5830  8.6000  5.2100 
Angles (°):  90  91.03  90 

Symmetry (theoretical): 

Space group:  15  C2/c 
Lattice parameters (Å):  14.5565  14.5565  5.1125 
Angles (°):  89.25  90.74  146.35 

Cell contents: 

Number of atoms:  60 
Number of atom types: 
Chemical composition: 

Atomic positions (theoretical):

Na:  0.3530  0.0225  0.1132 
Na:  0.3680  0.3680  0.7500 
Li:  0.0062  0.0062  0.2500 
Ti:  0.5707  0.2433  0.6246 
Si:  0.6697  0.1424  0.2916 
Si:  0.1906  0.0076  0.5388 
O:  0.2292  0.7999  0.4429 
O:  0.4781  0.0506  0.7480 
O:  0.3753  0.1255  0.4810 
O:  0.1653  0.0932  0.5114 
O:  0.5586  0.2906  0.9379 
O:  0.1434  0.9242  0.8251 
O:  0.6213  0.2089  0.2896 
O:  0.4363  0.3478  0.1237 
H:  0.3518  0.2666  0.2589 
H:  0.4800  0.3234  0.0722 
Na:  0.0225  0.3530  0.3868 
Ti:  0.2433  0.5707  0.8754 
Si:  0.1424  0.6697  0.2084 
Si:  0.0076  0.1906  0.9612 
O:  0.7999  0.2292  0.0571 
O:  0.0506  0.4781  0.7520 
O:  0.1255  0.3753  0.0190 
O:  0.0932  0.1653  0.9886 
O:  0.2906  0.5586  0.5621 
O:  0.9242  0.1434  0.6749 
O:  0.2089  0.6213  0.2104 
O:  0.3478  0.4363  0.3763 
H:  0.2666  0.3518  0.2411 
H:  0.3234  0.4800  0.4278 
Na:  0.6470  0.9775  0.8868 
Na:  0.6320  0.6320  0.2500 
Li:  0.9938  0.9938  0.7500 
Ti:  0.4293  0.7567  0.3754 
Si:  0.3303  0.8576  0.7084 
Si:  0.8094  0.9924  0.4612 
O:  0.7708  0.2001  0.5571 
O:  0.5219  0.9494  0.2520 
O:  0.6247  0.8745  0.5190 
O:  0.8347  0.9068  0.4886 
O:  0.4414  0.7094  0.0621 
O:  0.8566  0.0758  0.1749 
O:  0.3787  0.7911  0.7104 
O:  0.5637  0.6522  0.8763 
H:  0.6482  0.7334  0.7411 
H:  0.5200  0.6766  0.9278 
Na:  0.9775  0.6470  0.6132 
Ti:  0.7567  0.4293  0.1246 
Si:  0.8576  0.3303  0.7916 
Si:  0.9924  0.8094  0.0388 
O:  0.2001  0.7708  0.9429 
O:  0.9494  0.5219  0.2480 
O:  0.8745  0.6247  0.9810 
O:  0.9068  0.8347  0.0114 
O:  0.7094  0.4414  0.4379 
O:  0.0758  0.8566  0.3251 
O:  0.7911  0.3787  0.7896 
O:  0.6522  0.5637  0.6237 
H:  0.7334  0.6482  0.7589 
H:  0.6766  0.5200  0.5722 
Atom type 

We have listed here the reduced coordinates of all the atoms in the primitive unit cell.
It is enough to know only the position of the atoms from the assymetrical unit cell and then use the symmetry to build the whole crystal structure.

Visualization of the crystal structure: 

Size:

  
Nx:  Ny:  Nz:    
You can define the size of the supercell to be displayed in the jmol panel as integer translations along the three crys­tallo­gra­phic axis.
Please note that the structure is represented using the pri­mi­tive cell, and not the conventional one.