-    MROSEITE     -    CaTeO2CO3

 

Crystal Structure 


Because of the translational symmetry all the calculations are performed in the primitive unit cell and not in the conventional unit cell. The following information regarding the structure is given with respect to this primitive unit cell, which sometimes can take an unintuitive shape.

Symmetry (experimental): 

Space group:  61  Pbca 
Lattice parameters (Å):  6.9880  11.2010  10.5660 
Angles (°):  90  90  90 

Symmetry (theoretical): 

Space group:  61  Pbca 
Lattice parameters (Å):  7.0364  11.1512  10.5403 
Angles (°):  90  90  90 

Cell contents: 

Number of atoms:  64 
Number of atom types: 
Chemical composition: 

Atomic positions (theoretical):

Ca:  0.0000  0.0000  0.0000 
Te:  0.0000  0.0000  0.5000 
C:  0.6682  0.3318  0.7374 
O:  0.6643  0.3357  0.2496 
O:  0.3886  0.1850  0.2941 
O:  0.7883  0.2117  0.1644 
O:  0.3318  0.6682  0.2626 
O:  0.3357  0.6643  0.7504 
Ca:  0.1850  0.3886  0.7059 
Te:  0.2117  0.7883  0.8356 
C:  0.6114  0.8150  0.7059 
O:  0.8150  0.6114  0.2941 
O:  0.0000  0.0000  0.0000 
O:  0.0000  0.0000  0.0000 
O:  0.0000  0.0000  0.0000 
O:  0.0000  0.0000  0.0000 
Ca:  0.0000  0.0000  0.0000 
Te:  0.0000  0.0000  0.0000 
C:  0.0000  0.0000  0.0000 
O:  0.0000  0.0000  0.0000 
O:  0.0000  0.0000  0.0000 
O:  0.0000  0.0000  0.0000 
O:  0.0000  0.0000  0.0000 
O:  0.0000  0.0000  0.0000 
Ca:  0.0000  0.0000  0.0000 
Te:  0.0000  0.0000  0.0000 
C:  0.0000  0.0000  0.0000 
O:  0.0000  0.0000  0.0000 
O:  0.0000  0.0000  0.0000 
O:  0.0000  0.0000  0.0000 
O:  0.0000  0.0000  0.0000 
O:  0.0000  0.0000  0.0000 
Ca:  0.0000  0.0000  0.0000 
Te:  0.0000  0.0000  0.0000 
C:  0.0000  0.0000  0.0000 
O:  0.0000  0.0000  0.0000 
O:  0.0000  0.0000  0.0000 
O:  0.0000  0.0000  0.0000 
O:  0.0000  0.0000  0.0000 
O:  0.0000  0.0000  0.0000 
Ca:  0.0000  0.0000  0.0000 
Te:  0.0000  0.0000  0.0000 
C:  0.0000  0.0000  0.0000 
O:  0.0000  0.0000  0.0000 
O:  0.0000  0.0000  0.0000 
O:  0.0000  0.0000  0.0000 
O:  0.0000  0.0000  0.0000 
O:  0.0000  0.0000  0.0000 
Ca:  0.0000  0.0000  0.0000 
Te:  0.0000  0.0000  0.0000 
C:  0.0000  0.0000  0.0000 
O:  0.0000  0.0000  0.0000 
O:  0.0000  0.0000  0.0000 
O:  0.0000  0.0000  0.0000 
O:  0.0000  0.0000  0.0000 
O:  0.0000  0.0000  0.0000 
Ca:  0.0000  0.0000  0.0000 
Te:  0.0000  0.0000  0.0000 
C:  0.0000  0.0000  0.0000 
O:  0.0000  0.0000  0.0000 
O:  0.0000  0.0000  0.0000 
O:  0.0000  0.0000  0.0000 
O:  0.0000  0.0000  0.0000 
O:  0.0000  0.0000  0.0000 
Atom type 

We have listed here the reduced coordinates of all the atoms in the primitive unit cell.
It is enough to know only the position of the atoms from the assymetrical unit cell and then use the symmetry to build the whole crystal structure.

Visualization of the crystal structure: 

Size:

  
Nx:  Ny:  Nz:    
You can define the size of the supercell to be displayed in the jmol panel as integer translations along the three crys­tallo­gra­phic axis.
Please note that the structure is represented using the pri­mi­tive cell, and not the conventional one.