-    PYROPE     -    Mg3Al2(SiO4)3

 

Crystal Structure 


Because of the translational symmetry all the calculations are performed in the primitive unit cell and not in the conventional unit cell. The following information regarding the structure is given with respect to this primitive unit cell, which sometimes can take an unintuitive shape.

Symmetry (experimental): 

Space group:  230  Ia-3d 
Lattice parameters (Å):  11.4545  11.4545  11.4545 
Angles (°):  90  90  90 

Symmetry (theoretical): 

Space group:  230  Ia-3d 
Lattice parameters (Å):  0.5292  0.5292  0.5292 
Angles (°):  109.47  109.47  109.47 

Cell contents: 

Number of atoms:  80 
Number of atom types: 
Chemical composition: 

Atomic positions (theoretical):

Si:  0.2500  0.6250  0.3750 
Al:  0.0000  0.0000  0.0000 
Mg:  0.2500  0.3750  0.1250 
O:  0.7021  0.6859  0.0817 
Si:  0.3750  0.2500  0.6250 
Mg:  0.1250  0.2500  0.3750 
O:  0.0817  0.7021  0.6859 
Si:  0.7500  0.8750  0.1250 
Al:  0.5000  0.0000  0.5000 
Mg:  0.7500  0.1250  0.3750 
O:  0.1042  0.6204  0.4183 
Al:  0.0000  0.5000  0.5000 
O:  0.3958  0.8141  0.5162 
Si:  0.6250  0.7500  0.3750 
Al:  0.5000  0.0000  0.0000 
Mg:  0.3750  0.7500  0.1250 
O:  0.8796  0.3958  0.0817 
Si:  0.6250  0.3750  0.2500 
Mg:  0.3750  0.1250  0.2500 
O:  0.6859  0.0817  0.7021 
Si:  0.1250  0.7500  0.8750 
Al:  0.5000  0.5000  0.0000 
O:  0.4183  0.1042  0.6204 
O:  0.5162  0.3958  0.8141 
Si:  0.3750  0.6250  0.7500 
Al:  0.0000  0.5000  0.0000 
Mg:  0.1250  0.3750  0.7500 
O:  0.0817  0.8796  0.3958 
O:  0.7979  0.8796  0.9838 
Si:  0.8750  0.2500  0.1250 
Al:  0.5000  0.5000  0.5000 
O:  0.8141  0.7979  0.4183 
O:  0.9838  0.7979  0.8796 
O:  0.6859  0.1042  0.9838 
Si:  0.7500  0.3750  0.6250 
O:  0.1042  0.9838  0.6859 
Al:  0.0000  0.0000  0.5000 
O:  0.6204  0.7021  0.5162 
Si:  0.8750  0.1250  0.7500 
O:  0.6204  0.4183  0.1042 
O:  0.8141  0.5162  0.3958 
O:  0.3958  0.0817  0.8796 
Si:  0.1250  0.8750  0.2500 
O:  0.4183  0.8141  0.7979 
O:  0.8796  0.9838  0.7979 
O:  0.9838  0.6859  0.1042 
O:  0.5162  0.6204  0.7021 
Si:  0.2500  0.1250  0.8750 
O:  0.7979  0.4183  0.8141 
O:  0.7021  0.5162  0.6204 
Mg:  0.7500  0.6250  0.8750 
O:  0.2979  0.3141  0.9183 
Mg:  0.8750  0.7500  0.6250 
O:  0.9183  0.2979  0.3141 
Mg:  0.2500  0.8750  0.6250 
O:  0.8958  0.3796  0.5817 
O:  0.6042  0.1859  0.4838 
Mg:  0.6250  0.2500  0.8750 
O:  0.1204  0.6042  0.9183 
Mg:  0.6250  0.8750  0.7500 
O:  0.3141  0.9183  0.2979 
O:  0.5817  0.8958  0.3796 
O:  0.4838  0.6042  0.1859 
Mg:  0.8750  0.6250  0.2500 
O:  0.9183  0.1204  0.6042 
O:  0.2021  0.1204  0.0162 
O:  0.1859  0.2021  0.5817 
O:  0.0162  0.2021  0.1204 
O:  0.3141  0.8958  0.0162 
O:  0.8958  0.0162  0.3141 
O:  0.3796  0.2979  0.4838 
O:  0.3796  0.5817  0.8958 
O:  0.1859  0.4838  0.6042 
O:  0.6042  0.9183  0.1204 
O:  0.5817  0.1859  0.2021 
O:  0.1204  0.0162  0.2021 
O:  0.0162  0.3141  0.8958 
O:  0.4838  0.3796  0.2979 
O:  0.2021  0.5817  0.1859 
O:  0.2979  0.4838  0.3796 
Atom type 

We have listed here the reduced coordinates of all the atoms in the primitive unit cell.
It is enough to know only the position of the atoms from the assymetrical unit cell and then use the symmetry to build the whole crystal structure.

Visualization of the crystal structure: 

Size:

  
Nx:  Ny:  Nz:    
You can define the size of the supercell to be displayed in the jmol panel as integer translations along the three crys­tallo­gra­phic axis.
Please note that the structure is represented using the pri­mi­tive cell, and not the conventional one.