-    Na3H(SO4)2     -    Na3H(SO4)2

 

Crystal Structure 


Because of the translational symmetry all the calculations are performed in the primitive unit cell and not in the conventional unit cell. The following information regarding the structure is given with respect to this primitive unit cell, which sometimes can take an unintuitive shape.

Symmetry (experimental): 

Space group:  P1 
Lattice parameters (Å):  8.6330  9.6170  9.0820 
Angles (°):  89.988  108.80  90.05 

Symmetry (theoretical): 

Space group:  P1 
Lattice parameters (Å):  8.5678  9.6132  9.1394 
Angles (°):  89.99  108.51  90.001 

Cell contents: 

Number of atoms:  56 
Number of atom types: 
Chemical composition: 

Atomic positions (theoretical):

S:  0.1403  0.3072  0.8580 
S:  0.6306  0.3196  0.4019 
S:  0.1404  0.1900  0.3581 
S:  0.3679  0.8198  0.0881 
S:  0.8581  0.6904  0.1318 
S:  0.3678  0.6776  0.5879 
S:  0.8581  0.8071  0.6317 
S:  0.6306  0.1779  0.9021 
Na:  0.9991  0.9988  0.9946 
Na:  0.4989  0.9982  0.4943 
Na:  0.7357  0.9975  0.2657 
Na:  0.3826  0.1567  0.1262 
Na:  0.9991  0.4985  0.4950 
Na:  0.4994  0.4986  0.9955 
Na:  0.2626  0.4976  0.2242 
Na:  0.6159  0.6564  0.3637 
Na:  0.2626  0.9997  0.7242 
Na:  0.6158  0.8410  0.8637 
Na:  0.7357  0.4999  0.7657 
Na:  0.3828  0.3407  0.6262 
O:  0.1574  0.1550  0.8752 
O:  0.2565  0.3747  0.9931 
O:  0.9656  0.3456  0.8532 
O:  0.1608  0.3566  0.7148 
O:  0.6080  0.3612  0.5474 
O:  0.8101  0.3360  0.4187 
O:  0.5855  0.1730  0.3652 
O:  0.5352  0.4105  0.2755 
O:  0.1575  0.3422  0.3752 
O:  0.2566  0.1224  0.4931 
O:  0.9657  0.1517  0.3533 
O:  0.1609  0.1407  0.2148 
O:  0.3907  0.8614  0.9427 
O:  0.1883  0.8362  0.0709 
O:  0.4128  0.6731  0.1248 
O:  0.4631  0.9106  0.2145 
O:  0.8410  0.8425  0.1145 
O:  0.7418  0.6228  0.9967 
O:  0.0327  0.6520  0.1366 
O:  0.8375  0.6411  0.2750 
O:  0.3906  0.6362  0.4424 
O:  0.1881  0.6612  0.5707 
O:  0.4126  0.8243  0.6247 
O:  0.4630  0.5867  0.7142 
O:  0.8410  0.6549  0.6146 
O:  0.7418  0.8746  0.4966 
O:  0.0327  0.8454  0.6364 
O:  0.8376  0.8564  0.7749 
O:  0.6081  0.1365  0.0477 
O:  0.8102  0.1615  0.9190 
O:  0.5856  0.3245  0.8653 
O:  0.5353  0.0869  0.7759 
H:  0.8912  0.2582  0.8841 
H:  0.8913  0.2390  0.3839 
H:  0.1072  0.7394  0.1058 
H:  0.1073  0.7579  0.6056 
Atom type 

We have listed here the reduced coordinates of all the atoms in the primitive unit cell.
It is enough to know only the position of the atoms from the assymetrical unit cell and then use the symmetry to build the whole crystal structure.

Visualization of the crystal structure: 

Size:

  
Nx:  Ny:  Nz:    
You can define the size of the supercell to be displayed in the jmol panel as integer translations along the three crys­tallo­gra­phic axis.
Please note that the structure is represented using the pri­mi­tive cell, and not the conventional one.