-    PABSTITE     -    BaSnSi3O9

Theoretical atomic positions and lattice parameters at experimental volum from AMCSD. Tetter norm-conserving pseudopotential for Ba. 

Crystal Structure 


Because of the translational symmetry all the calculations are performed in the primitive unit cell and not in the conventional unit cell. The following information regarding the structure is given with respect to this primitive unit cell, which sometimes can take an unintuitive shape.

Symmetry (experimental): 

Space group:  188  P-6c2 
Lattice parameters (Å):  6.7420  6.7420  9.9300 
Angles (°):  90  90  120 

Symmetry (theoretical): 

Space group:  188  P-6c2 
Lattice parameters (Å):  6.7637  6.7637  9.8665 
Angles (°):  90  90  120 

Cell contents: 

Number of atoms:  28 
Number of atom types: 
Chemical composition: 

Atomic positions (theoretical):

Ba:  0.6667  0.3333  0.0000 
Sn:  0.3333  0.6667  0.0000 
Si:  0.0727  0.2870  0.2500 
O:  0.2483  0.1861  0.2500 
O:  0.0892  0.4264  0.1142 
Ba:  0.6667  0.3333  0.5000 
Sn:  0.3333  0.6667  0.5000 
Si:  0.7130  0.7857  0.2500 
O:  0.8139  0.0622  0.2500 
O:  0.5736  0.6628  0.3858 
Si:  0.7130  0.9273  0.7500 
O:  0.8139  0.7517  0.7500 
O:  0.5736  0.9108  0.8858 
Si:  0.2143  0.9273  0.2500 
O:  0.9378  0.7517  0.2500 
O:  0.3372  0.9108  0.1142 
Si:  0.0727  0.7857  0.7500 
O:  0.2483  0.0622  0.7500 
O:  0.0892  0.6628  0.6142 
Si:  0.2143  0.2870  0.7500 
O:  0.9378  0.1861  0.7500 
O:  0.3372  0.4264  0.6142 
O:  0.0892  0.4264  0.3858 
O:  0.3372  0.4264  0.8858 
O:  0.0892  0.6628  0.8858 
O:  0.3372  0.9108  0.3858 
O:  0.5736  0.6628  0.1142 
O:  0.5736  0.9108  0.6142 
Atom type 

We have listed here the reduced coordinates of all the atoms in the primitive unit cell.
It is enough to know only the position of the atoms from the assymetrical unit cell and then use the symmetry to build the whole crystal structure.

Visualization of the crystal structure: 

Size:

Nx:  Ny:  Nz: 
You can define the size of the supercell to be displayed in the jmol panel as integer translations along the three crys­tallo­gra­phic axis.
Please note that the structure is represented using the pri­mi­tive cell, and not the conventional one.
   

Dielectric Properties 


We define:

  • The Born effective charges, also called dynamical charges, are tensors that correspond to the energy derivative with respect to atomic displacements and electric fields or, equivalently, to the change in atomic force due to an electric field: The sum of the Born effective charges of all nuclei in one cell must vanish, element by element, along each of the three directions of the space.
  • The dielectric tensors are the energy derivative with respect to two electric fields. They also relate the induced polarization to the external electric field.

Born effective charges (Z): 

Ba: 2.8842 0.0000 -0.0000 
0.0000 2.8842 0.0000 
0.0000 0.0000 2.3575 
Eig. Value: 2.8842 2.8842 2.3575 
Sn: 3.8900 0.0000 -0.0000 
-0.0000 3.8900 0.0000 
-0.0000 0.0000 4.3955 
Eig. Value: 3.8900 3.8900 4.3955 
Si: 2.9364 -0.1272 0.0000 
-0.2860 3.6048 0.0000 
0.0000 0.0000 3.1512 
Eig. Value: 2.8777 3.6635 3.1512 
O: -2.1679 0.7370 0.0000 
0.7729 -2.1143 0.0000 
0.0000 -0.0000 -1.0400 
Eig. Value: -2.8965 -1.3857 -1.0400 
O: -1.5517 -0.1361 -0.1299 
-0.0794 -1.8359 0.6697 
-0.1566 0.6188 -2.1811 
Eig. Value: -1.6471 -1.2441 -2.6775 
Ba: 2.8842 0.0000 0.0000 
0.0000 2.8842 -0.0000 
-0.0000 -0.0000 2.3575 
Eig. Value: 2.8842 2.8842 2.3575 
Sn: 3.8900 0.0000 0.0000 
-0.0000 3.8900 -0.0000 
0.0000 -0.0000 4.3955 
Eig. Value: 3.8900 3.8900 4.3955 
Si: 3.2588 0.4721 0.0000 
0.3133 3.2824 0.0000 
-0.0000 -0.0000 3.1512 
Eig. Value: 2.8777 3.6635 3.1512 
O: -1.4739 -0.3722 0.0000 
-0.3364 -2.8083 0.0000 
-0.0000 -0.0000 -1.0400 
Eig. Value: -1.3857 -2.8965 -1.0400 
O: -1.8581 -0.0975 0.5150 
-0.0408 -1.5295 0.4473 
0.4576 0.4450 -2.1811 
Eig. Value: -1.6471 -1.2441 -2.6775 
Si: 3.6166 0.1067 0.0000 
0.2655 2.9246 0.0000 
-0.0000 0.0000 3.1512 
Eig. Value: 3.6635 2.8777 3.1512 
O: -2.7815 0.4186 -0.0000 
0.3827 -1.5007 0.0000 
-0.0000 0.0000 -1.0400 
Eig. Value: -2.8965 -1.3857 -1.0400 
O: -1.6715 -0.1485 0.6449 
-0.2053 -1.7161 0.2223 
0.6142 0.1738 -2.1811 
Eig. Value: -1.2441 -1.6471 -2.6775 
Si: 3.6166 -0.1067 -0.0000 
-0.2655 2.9246 0.0000 
-0.0000 0.0000 3.1512 
Eig. Value: 3.6635 2.8777 3.1512 
O: -2.7815 -0.4186 0.0000 
-0.3827 -1.5007 -0.0000 
-0.0000 0.0000 -1.0400 
Eig. Value: -2.8965 -1.3857 -1.0400 
O: -1.6715 0.1485 0.6449 
0.2053 -1.7161 -0.2223 
0.6142 -0.1738 -2.1811 
Eig. Value: -1.2441 -1.6471 -2.6775 
Si: 3.2588 -0.4721 0.0000 
-0.3133 3.2824 0.0000 
0.0000 0.0000 3.1512 
Eig. Value: 2.8777 3.6635 3.1512 
O: -1.4739 0.3722 -0.0000 
0.3364 -2.8083 -0.0000 
-0.0000 -0.0000 -1.0400 
Eig. Value: -1.3857 -2.8965 -1.0400 
O: -1.8581 0.0975 0.5150 
0.0408 -1.5295 -0.4473 
0.4576 -0.4450 -2.1811 
Eig. Value: -1.6471 -1.2441 -2.6775 
Si: 2.9364 0.1272 0.0000 
0.2860 3.6048 0.0000 
0.0000 -0.0000 3.1512 
Eig. Value: 2.8777 3.6635 3.1512 
O: -2.1679 -0.7370 0.0000 
-0.7729 -2.1143 0.0000 
-0.0000 -0.0000 -1.0400 
Eig. Value: -2.8965 -1.3857 -1.0400 
O: -1.5517 0.1361 0.1299 
0.0794 -1.8359 0.6697 
0.1566 0.6188 -2.1811 
Eig. Value: -1.6471 -1.2441 -2.6775 
O: -1.5517 -0.1361 0.1299 
-0.0794 -1.8359 -0.6697 
0.1566 -0.6188 -2.1811 
Eig. Value: -1.6471 -1.2441 -2.6775 
O: -1.5517 0.1361 -0.1299 
0.0794 -1.8359 -0.6697 
-0.1566 -0.6188 -2.1811 
Eig. Value: -1.6471 -1.2441 -2.6775 
O: -1.8581 0.0975 -0.5150 
0.0408 -1.5295 0.4473 
-0.4576 0.4450 -2.1811 
Eig. Value: -1.6471 -1.2441 -2.6775 
O: -1.6715 0.1485 -0.6449 
0.2053 -1.7161 0.2223 
-0.6142 0.1738 -2.1811 
Eig. Value: -1.2441 -1.6471 -2.6775 
O: -1.8581 -0.0975 -0.5150 
-0.0408 -1.5295 -0.4473 
-0.4576 -0.4450 -2.1811 
Eig. Value: -1.6471 -1.2441 -2.6775 
O: -1.6715 -0.1485 -0.6449 
-0.2053 -1.7161 -0.2223 
-0.6142 -0.1738 -2.1811 
Eig. Value: -1.2441 -1.6471 -2.6775 
Atom type 

Dielectric tensors: 

 
Ɛ2.8460 0.0000 0.0000 
0.0000 2.8460 0.0000 
0.0000 0.0000 2.8380 
Eig. Value: 2.8460 2.8460 2.8380 
Refractive index (N): 1.6870 0.0000 0.0000 
0.0000 1.6870 0.0000 
0.0000 0.0000 1.6846 
Eig. Value: 1.6870 1.6870 1.6846 
Ɛ00.0000 0.0000 0.0000 
0.0000 0.0000 0.0000 
0.0000 0.0000 0.0000 
Eig. Value: 0.0000 0.0000 0.0000