-    Na2S2O7     -    Na2S2O7

Theoretical atomic positions and lattice parameters at experimental volum from ICSD database; code 413049 

Crystal Structure 


Because of the translational symmetry all the calculations are performed in the primitive unit cell and not in the conventional unit cell. The following information regarding the structure is given with respect to this primitive unit cell, which sometimes can take an unintuitive shape.

Symmetry (experimental): 

Space group:  P-1 
Lattice parameters (Å):  6.7702  6.7975  6.7292 
Angles (°):  116.77  96.089  84.00 

Symmetry (theoretical): 

Space group:  P-1 
Lattice parameters (Å):  6.7920  6.8454  6.6806 
Angles (°):  116.74  97.13  82.68 

Cell contents: 

Number of atoms:  22 
Number of atom types: 
Chemical composition: 

Atomic positions (theoretical):

Na:  0.1485  0.8376  0.7804 
Na:  0.6683  0.7559  0.3834 
S:  0.1605  0.7575  0.2701 
S:  0.3586  0.3185  0.1436 
O:  0.0133  0.7324  0.3945 
O:  0.6653  0.1478  0.5861 
O:  0.9176  0.1447  0.8774 
O:  0.7664  0.4854  0.9118 
O:  0.6475  0.8575  0.0814 
O:  0.2459  0.2947  0.2986 
O:  0.4459  0.6052  0.7674 
Na:  0.8515  0.1624  0.2196 
Na:  0.3317  0.2441  0.6166 
S:  0.8395  0.2425  0.7299 
S:  0.6414  0.6815  0.8564 
O:  0.9867  0.2676  0.6055 
O:  0.3347  0.8522  0.4139 
O:  0.0824  0.8553  0.1226 
O:  0.2336  0.5146  0.0882 
O:  0.3525  0.1425  0.9186 
S:  0.7541  0.7053  0.7014 
O:  0.5541  0.3948  0.2326 
Atom type 

We have listed here the reduced coordinates of all the atoms in the primitive unit cell.
It is enough to know only the position of the atoms from the assymetrical unit cell and then use the symmetry to build the whole crystal structure.

Visualization of the crystal structure: 

Size:

Nx:  Ny:  Nz: 
You can define the size of the supercell to be displayed in the jmol panel as integer translations along the three crys­tallo­gra­phic axis.
Please note that the structure is represented using the pri­mi­tive cell, and not the conventional one.
   

Dielectric Properties 


We define:

  • The Born effective charges, also called dynamical charges, are tensors that correspond to the energy derivative with respect to atomic displacements and electric fields or, equivalently, to the change in atomic force due to an electric field: The sum of the Born effective charges of all nuclei in one cell must vanish, element by element, along each of the three directions of the space.
  • The dielectric tensors are the energy derivative with respect to two electric fields. They also relate the induced polarization to the external electric field.

Born effective charges (Z): 

Na: 1.1435 -0.1011 -0.0162 
0.0156 1.2049 -0.0586 
0.0381 -0.0655 1.1727 
Eig. Value: 1.1105 1.2665 1.1441 
Na: 1.1829 0.1636 0.0152 
0.0749 1.0270 0.0113 
0.0079 -0.0169 1.2108 
Eig. Value: 1.2495 0.9623 1.2091 
S: 3.2133 -0.2531 -0.3081 
-0.2941 3.3642 0.6621 
0.0714 -0.0257 3.1395 
Eig. Value: 3.0725 3.7494 2.8952 
S: 3.1268 -0.2416 0.1520 
-0.2682 3.5523 -0.2267 
-0.2082 0.4512 2.8904 
Eig. Value: 3.0110 3.6878 2.8707 
O: -1.5269 -0.2240 0.4602 
-0.0696 -0.9142 -0.0214 
0.3702 0.1560 -1.1625 
Eig. Value: -1.8261 -0.8651 -0.9125 
O: -1.4325 -0.0779 -0.3572 
-0.1906 -0.9661 -0.3139 
-0.4571 -0.1282 -1.2517 
Eig. Value: -1.8284 -0.8249 -0.9971 
O: -0.9596 0.2687 -0.1119 
0.2332 -1.5993 0.4501 
-0.1518 0.4367 -1.1733 
Eig. Value: -0.8646 -1.9582 -0.9094 
O: -1.0653 0.7491 0.2461 
0.7876 -2.4684 -0.5340 
0.2059 -0.5208 -1.0999 
Eig. Value: -0.7262 -2.9822 -0.9252 
O: -0.8548 0.0564 0.0230 
0.0358 -1.1202 -0.4393 
-0.0201 -0.3926 -1.6360 
Eig. Value: -0.8283 -0.9146 -1.8681 
O: -1.1167 -0.2002 0.2402 
-0.3534 -1.1691 0.4265 
0.3453 0.2207 -1.1699 
Eig. Value: -0.8649 -1.7495 -0.8413 
O: -1.7107 -0.1399 -0.3433 
0.0288 -0.9111 0.0438 
-0.2016 -0.1150 -0.9201 
Eig. Value: -1.8000 -0.9106 -0.8313 
Na: 1.1435 -0.1011 -0.0162 
0.0156 1.2049 -0.0586 
0.0381 -0.0655 1.1727 
Eig. Value: 1.1105 1.2665 1.1441 
Na: 1.1829 0.1636 0.0152 
0.0749 1.0270 0.0113 
0.0079 -0.0169 1.2108 
Eig. Value: 1.2495 0.9623 1.2091 
S: 3.2133 -0.2531 -0.3081 
-0.2941 3.3642 0.6621 
0.0714 -0.0257 3.1395 
Eig. Value: 3.0725 3.7494 2.8952 
S: 3.1268 -0.2416 0.1520 
-0.2682 3.5523 -0.2267 
-0.2082 0.4512 2.8904 
Eig. Value: 3.0110 3.6878 2.8707 
O: -1.5269 -0.2240 0.4602 
-0.0696 -0.9142 -0.0214 
0.3702 0.1560 -1.1625 
Eig. Value: -1.8261 -0.8651 -0.9125 
O: -1.4325 -0.0779 -0.3572 
-0.1906 -0.9661 -0.3139 
-0.4571 -0.1282 -1.2517 
Eig. Value: -1.8284 -0.8249 -0.9971 
O: -0.9596 0.2687 -0.1119 
0.2332 -1.5993 0.4501 
-0.1518 0.4367 -1.1733 
Eig. Value: -0.8646 -1.9582 -0.9094 
O: -1.0653 0.7491 0.2461 
0.7876 -2.4684 -0.5340 
0.2059 -0.5208 -1.0999 
Eig. Value: -0.7262 -2.9822 -0.9252 
O: -0.8548 0.0564 0.0230 
0.0358 -1.1202 -0.4393 
-0.0201 -0.3926 -1.6360 
Eig. Value: -0.8283 -0.9146 -1.8681 
S: -1.1167 -0.2002 0.2402 
-0.3534 -1.1691 0.4265 
0.3453 0.2207 -1.1699 
Eig. Value: -0.8649 -1.7495 -0.8413 
O: -1.7107 -0.1399 -0.3433 
0.0288 -0.9111 0.0438 
-0.2016 -0.1150 -0.9201 
Eig. Value: -1.8000 -0.9106 -0.8313 
Atom type 

Dielectric tensors: 

 
Ɛ2.2696 0.0000 0.0000 
0.0000 2.3696 0.0532 
0.0000 0.0532 2.2638 
Eig. Value: 2.2696 2.3917 2.2416 
Refractive index (N): 1.5065 0.0000 0.0000 
0.0000 1.5393 0.2307 
0.0000 0.2307 1.5046 
Eig. Value: 1.5065 1.5465 1.4972 
Ɛ00.0000 0.0000 0.0000 
0.0000 0.0000 0.0000 
0.0000 0.0000 0.0000 
Eig. Value: 0.0000 0.0000 0.0000