-    BRAZILIANITE     -    NaAl3(PO4)2(OH)4

 

Crystal Structure 


Because of the translational symmetry all the calculations are performed in the primitive unit cell and not in the conventional unit cell. The following information regarding the structure is given with respect to this primitive unit cell, which sometimes can take an unintuitive shape.

Symmetry (experimental): 

Space group:  14  P2_1/n 
Lattice parameters (Å):  11.2330  10.1420  7.0970 
Angles (°):  90  97.37  90 

Symmetry (theoretical): 

Space group:  14  P2_1/n 
Lattice parameters (Å):  11.0300  9.9346  6.9763 
Angles (°):  90  97.73  90 

Cell contents: 

Number of atoms:  88 
Number of atom types:  5 
Chemical composition:  0 

Atomic positions (theoretical):

P:  0.1788  0.3126  0.2331 
P:  0.3088  0.3345  0.7518 
Al:  0.0430  0.2169  0.5626 
Al:  0.2656  0.0733  0.5098 
Al:  0.4595  0.2590  0.4311 
Na:  0.3084  0.0790  0.0455 
O:  0.1049  0.0785  0.4474 
O:  0.4239  0.1131  0.5724 
O:  0.0016  0.3474  0.7250 
O:  0.4967  0.3928  0.2685 
O:  0.1162  0.2331  0.0619 
O:  0.2888  0.2244  0.3209 
O:  0.2211  0.2190  0.6769 
O:  0.3851  0.2850  0.9354 
O:  0.0924  0.3409  0.3844 
O:  0.3895  0.3785  0.6000 
O:  0.2225  0.4501  0.1789 
O:  0.2278  0.4549  0.7865 
H:  0.0685  0.0050  0.3590 
H:  0.4707  0.1072  0.7026 
H:  0.0735  0.4044  0.7657 
H:  0.0488  0.0337  0.8316 
P:  0.3212  0.8126  0.2669 
P:  0.1912  0.8345  0.7482 
Al:  0.4570  0.7169  0.9374 
Al:  0.2344  0.5733  0.9902 
Al:  0.0405  0.7590  0.0689 
Na:  0.1916  0.5790  0.4545 
O:  0.3951  0.5785  0.0526 
O:  0.0761  0.6131  0.9276 
O:  0.4984  0.8474  0.7750 
O:  0.0033  0.8928  0.2315 
O:  0.3838  0.7331  0.4381 
O:  0.2112  0.7244  0.1791 
O:  0.2789  0.7190  0.8231 
O:  0.1149  0.7850  0.5646 
O:  0.4076  0.8409  0.1156 
O:  0.1105  0.8785  0.9000 
O:  0.2775  0.9501  0.3211 
O:  0.2722  0.9549  0.7135 
H:  0.4315  0.5050  0.1410 
H:  0.0293  0.6072  0.7974 
H:  0.4265  0.9044  0.7343 
H:  0.4512  0.5337  0.6684 
P:  0.8212  0.6874  0.7669 
P:  0.6912  0.6655  0.2482 
Al:  0.9570  0.7831  0.4374 
Al:  0.7344  0.9267  0.4902 
Al:  0.5405  0.7410  0.5689 
Na:  0.6916  0.9210  0.9545 
O:  0.8951  0.9215  0.5526 
O:  0.5761  0.8869  0.4276 
O:  0.9984  0.6526  0.2750 
O:  0.5033  0.6072  0.7315 
O:  0.8838  0.7669  0.9381 
O:  0.7112  0.7756  0.6791 
O:  0.7789  0.7810  0.3231 
O:  0.6149  0.7150  0.0646 
O:  0.9076  0.6591  0.6156 
O:  0.6105  0.6215  0.4000 
O:  0.7775  0.5499  0.8211 
O:  0.7722  0.5451  0.2135 
H:  0.9315  0.9950  0.6410 
H:  0.5293  0.8928  0.2974 
H:  0.9265  0.5956  0.2343 
H:  0.9512  0.9663  0.1684 
P:  0.6788  0.1874  0.7331 
P:  0.8088  0.1655  0.2518 
Al:  0.5430  0.2831  0.0626 
Al:  0.7656  0.4267  0.0098 
Al:  0.9595  0.2410  0.9311 
Na:  0.8084  0.4210  0.5455 
O:  0.6049  0.4215  0.9474 
O:  0.9239  0.3869  0.0724 
O:  0.5016  0.1526  0.2250 
O:  0.9967  0.1072  0.7685 
O:  0.6162  0.2669  0.5619 
O:  0.7888  0.2756  0.8209 
O:  0.7211  0.2810  0.1769 
O:  0.8851  0.2150  0.4354 
O:  0.5924  0.1591  0.8844 
O:  0.8895  0.1215  0.1000 
O:  0.7225  0.0499  0.6789 
O:  0.7278  0.0451  0.2865 
H:  0.5685  0.4950  0.8590 
H:  0.9707  0.3928  0.2026 
H:  0.5735  0.0956  0.2657 
H:  0.5488  0.4663  0.3316 
Atom type  X  Y  Z 

We have listed here the reduced coordinates of all the atoms in the primitive unit cell.
It is enough to know only the position of the atoms from the assymetrical unit cell and then use the symmetry to build the whole crystal structure.

Visualization of the crystal structure: 

Size:

 Nx:  Ny:  Nz: 
You can define the size of the supercell to be displayed in the jmol panel as integer translations along the three crys­tallo­gra­phic axis.
Please note that the structure is represented using the pri­mi­tive cell, and not the conventional one.